Rust-Oleum Noxyde Plus – High-Performance Elastic Anti-Corrosion Coating
Rust-Oleum Noxyde Plus is a highly flexible, single-pack water-based elastomeric coating designed for maximum adhesion and superior corrosion protection. Based on a silane-modified acrylic binder, this advanced formulation delivers a 200% elastic coat that won’t crack or peel, even under extreme movement. It offers excellent coverage of complex areas such as nuts, bolts, and welds, and features dry fall properties to minimize overspray clean-up. Ideal for protecting steel and other metal substrates, it's lead, chromate, and zinc free, making it safer for both users and the environment.
Key Features:
-
Superior Adhesion to metal and difficult substrates
-
200% Elasticity – Resists cracking and peeling
-
Dry Fall Formula – Reduces prep and cleanup time
-
Exceptional Coverage – Especially around bolts, welds, and fasteners
-
One Pack Water-Based System – Easy to apply, no mixing required
-
Low Dirt Pick-Up – Maintains clean appearance longer
-
Zinc-, Lead- & Chromate-Free – Safer, more eco-friendly formulation
Surface preparation
Remove grease, oil and all other surface contaminations by alkaline or high pressure
(steam) cleaning (max. 200 Bars) in combination with appropriate detergents. The
substrate has to be dust free and made rust free by means of sandblasting (Sa2), manual
cleaning (St2) or high pressure water jetting (min. 600 Bars). After jetting, the substrate
has to be dust free. On new galvanised surfaces, new zinc, aluminium, stainless steel,
apply first a coat of Pegalink or PVDF Primer. On ferrous substrates, apply Noxyde Plus in
red or grey as the first coat. In all instances apply contrasting Noxyde Plus colours for
subsequent layers.
Technical Data
Density (g/cm³): 1,25
Gloss Level: Satin
Gloss level at 60º: 24%
Solids Content in weight: 66%
Solids content in volume: 46%
Salt Spray Resistance: 1.248h salt spray resistance ISO 9227:2017
Test data: ABRASION RESISTANCE,METHOD: ASTM D4060
(CS-17 / 1,000g / 1,000 cycles)
RESULTS: 61 mg loss (Avg.)
IMPACT RESISTANCE, METHOD: ASTM 2794
RESULTS: Direct: 33.9 Nm (300 in-lbs.)
Indirect: 22.6 Nm (200 in-lbs.)
FLEXIBILITY, METHOD: ASTM 522 (Conical
Mandrel)
RESULTS: 52% (Avg.)
INITIAL ELONGATION,METHOD: ASTM D638
Averaged over 5 tests on films of 2-coats @ 7 mils
(175µ) each, cured for 14 days
RESULTS: @ 23 C. (73 F.) : 254%
@ 0 C. (32 F.) : 7.2%
INITIAL TENSILE STRENGTH, METHOD: ASTM D638
Averaged over 5 tests on 2-coats @ 7 mils (175µ)
each, cured for 21 days
RESULTS: @ 23 C. (73 F.) : 4.98N/mm2 (722.3
psi)
@ 0 C. (32 F.) : 18.7 N/mm2 (2,712.2
psi)
ADHESION, PULL-OFF, METHOD: DIN ISO 4624
/ASTM D4541 (SP-10 / Sa 2.5)
RESULTS: 5.2 MPa (754 psi) *Averaged over 9 tests
on 2-coats @ 7 mils (175µ) each, cured for 42 days
SALT SPRAY, METHOD: DIN EN ISO 9227 (ASTM
B117) @1,248 hours (SP-10 / Sa 2.5)
RESULTS: Blistering: 0 (None)
Rusting: 0 (None)
Delamination: 0 (None)
Corrosion: <0.5mm
Directions for Use
To ensure homogeneity, coating materials should be thoroughly stirred mechanically prior
to use.
APPLICATION & THINNING: BRUSH
Undiluted as a rust preventive paint. Diluted with up to 25% volume water as an adhesion
primer (consumption about 120 g/m² - max. 100 µm wet film thickness - 20 µm dry film
thickness)
APPLICATION & THINNING: ROLLER
Undiluted as a rust preventive paint. Diluted with up to 25% volume water as an adhesion
primer (consumption about 120 g/m² - max. 100 µm wet film thickness - 20 dry film
thickness)